(Created page with " =Scotch Tape -vs- Kapton tape== A 20 MeV electron was used to make a bremsstrahlung beam that impinged a sample of regular Scotch Tape and Kapton tape. Both tapes had similar…") |
|||
| Line 1: | Line 1: | ||
| − | =Scotch Tape -vs- Kapton tape== | + | ==Scotch Tape -vs- Kapton tape== |
A 20 MeV electron was used to make a bremsstrahlung beam that impinged a sample of regular Scotch Tape and Kapton tape. Both tapes had similar areas of 2.5 x 3 cm. The Kapton had twice as much mass as the Scotch (0.1247 g -vs 0.0699 g). | A 20 MeV electron was used to make a bremsstrahlung beam that impinged a sample of regular Scotch Tape and Kapton tape. Both tapes had similar areas of 2.5 x 3 cm. The Kapton had twice as much mass as the Scotch (0.1247 g -vs 0.0699 g). | ||
Revision as of 18:09, 22 September 2016
Scotch Tape -vs- Kapton tape
A 20 MeV electron was used to make a bremsstrahlung beam that impinged a sample of regular Scotch Tape and Kapton tape. Both tapes had similar areas of 2.5 x 3 cm. The Kapton had twice as much mass as the Scotch (0.1247 g -vs 0.0699 g).
The scotch taper became brittle after 4 hours of irradiation on the 25 N machine.
Below is an uncalibrated spectrum using Thorium rods. Lines should appear at 2614 and