Does salt change the amount of current?

The materials I used were

1. A half square foot sheet of copper flashing.

2. Two alligator clip leads.

3. A sensitive micro-ammeter that can read currents between 10 and 50 microamperes.

4. An electric stove or oven.

5. A large clear plastic bottle with the top cut off. I used a 2 liter spring water bottle. A large mouth glass jar will also work.

6. Table salt.

7. Tap water.

8. Sand paper or a wire brush.

9. A Paper cutter for cutting the copper sheet.

Solar cells are designed to convert light into electrical energy. They do this without the use of either chemical reactions or moving parts. Modern solar cells are based on semiconductors, a material whose electrical properties lie between conductors and insulators. In a conductor electric current can flow freely. In a insulator electric current can't flow freely. Light hitting a semiconductor solar cell pushes electrons out of the semiconductor making an electric current we can use.

I was unable to observe a dependence of the solar cell output current on the amount of salt I added.

The standard setup for my project is a plastic bottle that contains hot or cold water, salt, and 2 sheets of copper. One of the copper sheets was baked at a high temperature to convert the copper into cuprous oxide. The alligator clips are used to attached to the micro ammeter to the two copper sheets. The micro ammeter measures how much current flows between the two copper sheets.

I learned that the amount of salt doesn't change the current.

Making Cuprous Oxide

Cuprous oxide [math](Cu_2O)[/math] can be made by heating copper. Heating the copper causes the formation of both cuprous oxide and cupric oxide. Cupric oxide is dark black and is not what we want. Underneath the dark black cupric oxide is cuprous oxide. Cuprous oxide looks reddish. I first tried to make cuprous oxide using the top burner on an electric stove. As shown in the figure below, I did not see a lot of the reddish cuprous oxide formed.

A 6" x 6" copper flashing was baked in a 500 degree celsius oven for 20 Minutes.

Copper cuprousocideRed cupricoxideBlack 3-1-08.jpg

Copper cuprousocideRed 3-1-08.jpg

The picture below shows the difference between the two burnt copper sheets. The sheet on the left was baked at 500 celsius and the one on the right was cooked on a stove top. You can see that the baked copper sheet has more of the red cuprous oxide visible while the one burnt on the stove top has the red cuprous oxide located mostly in the lower half of the sheet.

CuprousoxideRed Compare.jpg


SolarCellApparatus 3-8-08.jpg


Ammeter NoSunlight.jpg Ammeter Sunlight.jpg

RawData 2-8-08.jpg

DiffData 2-8-08.jpg

ImersedIn1cmData 2-8-08.jpg