Difference between revisions of "PAA Nephrite Jadiete"
(4 intermediate revisions by the same user not shown) | |||
Line 273: | Line 273: | ||
==October 2017 Measurement== | ==October 2017 Measurement== | ||
− | Below is a table of the measurements made on October 16, 2017. | + | Below is a table of the measurements made on October 16, 2017. The files will be located on daq1 in the directory /data/IAC/Jade/Oct_2017 |
{| border="3" cellpadding="5" cellspacing="0" | {| border="3" cellpadding="5" cellspacing="0" | ||
| MPA Filename ||Date || Start|| Stop || Sample || Position | | MPA Filename ||Date || Start|| Stop || Sample || Position | ||
|- | |- | ||
− | ||AllJade_10_16_17.mpa || 10/16/17 || | + | ||AllJade_10_16_17.mpa || 10/16/17 ||11:12:13 ||12:20 ||4100.189 ||Pos 10 Det A |
+ | |- | ||
+ | ||Background_AccOff_10_16_17.mpa || 10/16/17 || 12:22:14 ||13:24||3726.294 || n/a | ||
|- | |- | ||
|} | |} | ||
+ | Using the Thorium rods the calibration constants are | ||
+ | |||
+ | <math> Slope = 1.02068 \pm 0.0000962 </math> | ||
+ | <math> Intercept = -12.4103 \pm 0.117 </math> | ||
[[PAA_Research]] | [[PAA_Research]] |
Latest revision as of 19:40, 16 October 2017
PAA on Jade
https://en.wikipedia.org/wiki/Jade#Nephrite_and_jadeite
Sample Information (Mayir Mamtimin)
The chemical formula for nephrite is
.Run Nmmber | Date | total time [sec] | Sample |
5875 | 02/10/17 17:48 | 4335 | KQT-1 |
5900 | 2/12/17 | 1759 | KQT-2 |
5901 | 2/12/17 | 1835 | UT-1 |
5902 | 2/12/17 | 1201 | UT-2 |
5904 | 2/12/17 | 671 | UT-3 |
5905 | 2/12/17 | 1114 | T-1 |
5906 | 2/12/17 | 967 | T-2 |
5907 | 2/12/17 | 931 | T-3 |
Run Number | Date | start time | end time | Position | Sample | runtime (s) |
5915 | 2/12/17 | 16:42:15 | 17:01 | 7 | UT-3 irradiation ended at 16:02 | 1131 |
Lines of interest
Reaction | ||
1779 | 2.2 min | |
1274 | 6.6 min | |
1369 | 15 hrs | |
377 | 8.5 min |
Relative Photon Dose Distribution as measured by the OSLs.
OSL Number | Initial (mRad) | X Position (cm) | Y Position (cm) | Final Dose (mRad) | Final - Initial Dose (mRad) |
386785 | 61 | -20.32 | 0 | 53681 | 53620 |
35358G | 60 | -15.24 | 0 | 103945 | 103885 |
321412 | 65 | -10.16 | 0 | 206000 | 205935 |
56332Q | 101 | -5.08 | 0 | 519683 | 519582 |
33143X | 63 | 0 | 0 | 1015938 | 1015875 |
40757D | 64 | 5.08 | 0 | 871016 | 870952 |
33432U | 65 | 10.16 | 0 | 418717 | 418652 |
31812Q | 294 | 15.24 | 0 | 174514 | 174220 |
330960 | 57 | 20.32 | 0 | 98713 | 98656 |
47799Z | 220 | 0 | 20.32 | 74781 | 74561 |
42413T | 61 | 0 | 15.24 | 150752 | 150691 |
31936E | 62 | 0 | 10.16 | 303013 | 302951 |
653995 | 183 | 0 | 5.08 | 599322 | 599139 |
42529E | 252 | 0 | -5.08 | 556382 | 556130 |
351401 | 60 | 0 | -10.16 | 209988 | 209928 |
31886B | 58 | 0 | -20.32 | 39653 | 39595 |
35312W | 65 | -20.32 | 20.32 | 27807 | 27742 |
31814M | 94 | -15.24 | 15.24 | 54535 | 54441 |
42127Q | 80 | -10.16 | 10.16 | 125909 | 125829 |
41762L | 63 | -5.08 | 5.08 | 382904 | 382841 |
32385M | 125 | 5.08 | -5.08 | 540179 | 540054 |
32739B | 103 | 10.16 | -10.16 | 130903 | 130800 |
33655I | 58 | 15.24 | -15.24 | 41572 | 41514 |
438784 | 123 | 20.32 | -20.32 | 22208 | 22085 |
40335R | 62 | -2.54 | 2.54 | 616421 | 616359 |
Irradiation info
2/14/2017
ADC #=1
MPA->Draw("evt.Chan>>(4000,0,4000)","ADCid==1");
Filename | Sample |
5875 | KQT-1 |
5900 | KQT-2 |
5901 | UT-1 |
5902 | UT-2 |
5904 | UT-3 |
5905 | T-1 |
5906 | T-2 |
5907 | T-3 |
4/18/2017
calibration : 0.491937+0.808439*evt.Chan For detector B
14:30: Ran 25B machine at 250 Hz, 90 mA, 4us Pulse Width, 21.5 MeV incident electrons for 1 hour, 870012 pulses.
Sample KQT-2 was placed right after Dans Pb-Ni sample.
File /data/IAC/Jade/Jade_4-18-17/JadeAccOff.txt is a 30 minute measurement 2 minutes after beam off
File /data/IAC/Jade/Jade_4-18-17/JadeAccOn.txt is a ~ 1 hour measurement after the accelerator was turned on and just after the above measurement ended.
I didn't see the Aluminum lines using
MPA->Draw("0.491937+0.808439*evt.Chan>>(4096,0,4096)","evt.ADCid==1");
Using the above calibration I see a line at 1766 leV with a half life of 2.56 min.
The blue line represents the counts observed after 480 second, the red line are the counts observed during the next 480 second time interval | A fit to the counts observed over the first 480 seconds |
I see Cl-40 line at 2220 keV with half life of 1.35 min
There is a 630 keV line with a 219 second half life (= ln(0.5)/-0.003155)
Possible reactions
I see a line at 142 +/- 2 keV with a half life of about 474 seconds (7.9 min)
16:00: ran Se-Foil 50-50 by mass mixture was irradiate using the same conditions as above for
October 2017 Measurement
Below is a table of the measurements made on October 16, 2017. The files will be located on daq1 in the directory /data/IAC/Jade/Oct_2017
MPA Filename | Date | Start | Stop | Sample | Position |
AllJade_10_16_17.mpa | 10/16/17 | 11:12:13 | 12:20 | 4100.189 | Pos 10 Det A |
Background_AccOff_10_16_17.mpa | 10/16/17 | 12:22:14 | 13:24 | 3726.294 | n/a |
Using the Thorium rods the calibration constants are